Release Property of Alginate Beads Coated with Poly(N-isopropylacrylamide-co-dimethylaminoethylmethacrylate)

초록

Alginate beads were coated with copolymers of N-isopropylacrylamide and dimethylaminoethylmethacrylate (P(NIPAM-co-DMAEMA)s) by taking advantage of electrostatic interaction between alginate and the copolymer. The copolymers, of which DMAEMA contents in the feed for the copolymerization were 5.0% (PND 5) and 15.0% (PND 15), were employed for the coatings of alginate beads. The adsorption curve of PND 5 and PND 15 on the surface of alginate beads seemed to be Langmuir isotherm. The beads were coated in the PND solutions (2%, pH 5.0 or pH 7.0) and the amounts of adsorption (g PND/g alginate) were about 1.3 with PND 5 solution (pH 5.0), 1.2 with PND 15 solution (pH 5.0), and 0.75 with PND 15 (pH 7.0). The release from the beads coated with PNDs were observed at 30 degrees C, 37 degrees C, and 45 degrees C using amaranth or FITC-dextran as a dye. The degrees of release were significantly suppressed due to the coating layers of PNDs. However, the coating layers could hardly act as a controller for the temperature-sensitive release.

키워드