Characterization and gas sensing properties of bead-like ZnO using multi-walled carbon nanotube templates

초록

We report bead-like ZnO nanostructures for gas sensing applications, synthesized using multi-walled carbon nanotube (MWCNT) templates. The ZnO nanostructures are grown following a two-step process: in the first, ZnO nanoparticles are synthesized on MWCNTs by thermal evaporation of a Zn powder; and in the second, the hybrid nanostructures are heat-treated at 800 °C. Scanning and transmission electron microscopy images indicate that the bead-like ZnO nanostructures have surface protuberances with nanoparticle sizes ranging from 20 to 60 nm, and a well-crystallized hexagonal structure. Gas sensors based on multiple-networked bead-like ZnO showed considerably enhanced electrical responses and better stability to both oxidizing (NO<inf>2</inf>) and reducing (CO) gases compared with previously reported nanostructured gas sensors, even if the response to CO gas was slow to increase. Both the NO<inf>2</inf> and CO gas sensing properties increased dramatically when the working temperature was increased up to 300 °C. The response sensitivities measured were 2953%, 5079%, 9641%, 3568%, and 3777% to 20 ppm NO<inf>2</inf> at 200, 250, 300, 350 and 400 °C, respectively. For CO gas on the other hand, the response sensitivities were 107%, 110%, 114%, 118%, and 122% at 5, 10, 20, 50, and 100 ppm concentrations, respectively. For concentrations between 5 and 20 ppm, the recovery time of the oxidizing gas was much shorter than the response time. The origin of the NO<inf>2</inf>/CO gas sensing mechanism of the bead-like ZnO nanostructures is discussed. © 2015 Elsevier Ltd. and Techna Group S.r.l. All rights reserved.

키워드