LiFePO4 분말 위 탄소나노튜브의 직접 성장과 리튬이온전지 양극재로의 적용

초록

We demonstrate a direct growth of carbon nanotubes (CNTs) on the surface of LiFePO4 (LFP) powders for use in lithium-ion batteries (LIB). LFP has been widely used as a cathode material due to its low cost and high stability. However, there is a still enough room for development to overcome its low energy density and electrical conductivity. In this study, we fabricated novel structured composites of LFP and CNTs (LFP-CNTs) and characterized the electrochemical properties of LIB. The composites were prepared by direct growth of CNTs on the surface of LFP using a rotary chemical vapor deposition. The growth temperature and rotation speed of the chamber were optimized at 600 °C and 5 rpm, respectively. For the LIB cell fabrication, a half-cell was fabricated using polytetrafluoroethylene (PTFE) and carbon black as binder and conductive additives, respectively. The electrochemical properties of LIBs using commercial carbon-coated LFP (LFP/C), LFP with CNTs grown for 10 (LFP/CNTs-10m) and 30 min(LFP/CNTs-30m) are comparatively investigated. For example, after the formation cycle, we obtained 149.3, 160.1, and 175.0 mAh/g for LFP/C, LFP/CNTs-10m, and LFP/CNTs-30m, respectively. In addition, the improved rate performance and 111.9 mAh/g capacity at 2C rate were achieved from the LFP/CNTs-30m sample compared to the LFP/CNTs-10m and LFP/C samples. We believe that the approach using direct growth of CNTs on LFP particles provides straightforward solution to improve the conductivity in the LFP-based electrode by constructing conduction pathways.

키워드