Effect of Glass Frit Addition on Characteristics of Yttria Ceramics

초록

The semiconductor and display industries require the development of plasma resistant materials for use in high density plasma etching process equipment. Yttria (Y2O3) is a ceramic material mainly used to ensure good plasma resistance properties, which requires a dense microstructure. In commercial production, a sintering process is applied to reduce the sintering temperature of Y2O3. In this study, the effect of the addition of glass frit to the sintered specimen was examined when manufacturing yttria sintered specimens for semiconductor process equipment parts. The Y2O3 specimen was shaped into a & Oslash;50 mm size and then sintered at 1,600 degrees C for 1 similar to 8 h. The characteristics, X-ray diffraction pattern, densities, contraction rate of the specimen, and swelling of the surface of the Y2O3 specimens were investigated as a function of the sintering time and glass frit addition. The Y2O3 specimen exhibited a density of over 4.9 g/cm(3) as the sintering time increased, and the swelling phenomenon characteristics were improved by glass frit, by controlling particle size.

키워드