신갈나무 정상재와 인장이상재의 전단 및 휨 파면해석

초록

This study has been carried out to understand the fracture characteristics of the tension wood of Quercus mongolica under the shear and bending stress. Macroscopically, the wood fluff in the shear surface appeared more frequently in tension wood than sound wood, and more coarse wood fluffs were observed in 30% than 10% moistured shear surface. In the fractured tension wood from bending stress, more thick and long wood fiber appeared than sound wood. The observation using scanning electron microscope indicated that both sound and tension wood samples from radial shear surface showed the intrawall dominated failure and the fracture surface of the ray parenchyma cell showed the transwall dominated failure. In tangential shear surface,wood fiber surface showed the intrawall failure and short and coarse wood fiber was observed in tension wood. Ray parenchyma cell of sound and tension wood samples showed the transwall failure. The surfaces of tension wood’s ray parenchyma cell were relatively clean. The fractured tension wood from bending stress showed unsharp and flat wood fiber compared with sound wood.

키워드