Effect of film thickness on the ferroelectric and dielectric properties of low-temperature (400 °C) Hf0.5Zr0.5O2 films

초록

We report on the effect of the Hf0.5Zr0.5O2 (HZO) film thickness on the ferroelectric and dielectric properties using pulse write/read measurements. HZO films of thicknesses ranging from 5 to 20 nm were annealed at 400 degrees C for 1min in a nitrogen ambient to be compatible with the back-end of the line thermal budget. As the HZO film thickness decreases, low-voltage operation (1.0V or less) can be achieved without the dead layer effect, although switching polarization (P-sw) tends to decrease due to the smaller grain size. Meanwhile, for 20-nm-thick HZO films prepared under the identical stress (similar TiN top electrode thickness and thermal budget), the Psw and dielectric constant are reduced because of additional monoclinic phase formation. Published by AIP Publishing.