재유화형 분말수지 혼입 폴리머 시멘트 모르타르의 건조수축 및 강도특성

초록

This study was conducted to investigate experimentally the drying shrinkage and the strength properties of redispersible SBR and PAE powder-modified mortars. Polymer-cement ratio, content of shrinkage-reducing agent and antifoamer content were manipulated as the experimental variables. The peculiarity of this study is to obtain a high early-age strength by using the portland cement and alumina cement with the ratio of 8 : 2. Until 7 days of age, the drying shrinkage remarkably increased up to 1∼2×10-4, while it tended to decrease as the ratio of polymer to cement ratio and the content of shrinkage-reducing agent increased. Polymer-cement ratio was effective in improving the flexural, tensile and adhesive strengths: As the ratio increased, the strengths correspondingly increased. The flexural strength was in the range of 7∼11 MPa, the tensile strength was 3.5∼5 MPa and the adhesive strength was 1.2∼3.9 MPa. On the other hand, the compressive strength tended to decrease as the polymer-cement ratio increased, and it was in the range of 23∼39 MPa. All strengths, flexural, tensile, adhesive and compressive strengths, decreased as the content of powder shrinkage-reducing agent increased. It turned out that the polymer-cement ratio influenced more on the behavior of drying shrinkage and the properties of strength than the powder shrinkage-reducing agent did.

키워드